T10A(T10、SK105/SK95、1.1645、C105W2)

1.Composition(wt%):

2.Properties:

3.Theory:

Since less content of alloying elements in steel, low tempering resistance, thus the bearing capacity is low, 
and hardenability is poor, quenching deformation is big.
High hardness and wear resistance.

4. Applications

1.Used to make general die, when batch is less 100000, soft washed material is low carbon steel whose
 material thickness is less than 1 mm.
2.Used in the manufacture of cold drawing, drawing die.
3.Used in the manufacture of long blade whose cutting thickness is 11 mm medium plate, after
 implementation of thin shell quenching,with high fatigue resistance, Collapse edge tending to be low, seven
 times higher than 9 CrWMn steel service life. 4.Used in  the holes of punch on the soft silicon steel sheet. 
5.Can be used to make terrace die of blanking die, concave die, panel board whose material thicknes
s is less than 3 mm; while making  terrace die, the hardness is 58—62HRC; when making die , the hardness is 60—64HRC.
6.Can be used to make general bending punch, concave die, set pieces，the hardness is 56—60HRC.
7.Manufacturing a general drawing die punch, concave die, set pieces, when asked tthe punch’s
 hardness is 58—62HRC；when making die choose 60-64 HRC hardness.
8.Manufacturing aluminum die of cold extrusion die, choose 62-64 HRC hardness.
9.Manufacturing all kinds of medium and small batch production of cold die, and integral cold heading die, 
punching and shearing tools, needed in thin shell hardening conditions   
10.Used for cold punch (punch), underload, dimensions, hardness of 58, 60 HRC;Used for hexagonal nut
 cold heading die, the hardness is 48—52HRC.
11.Used in wire drawing die and simple blanking die.
12.Used in all kinds of medium and small batch production of moulds and resistance to impact load.
13.Manufacturing long blade using 9CrWMn to make 11mm medium thickness steel plate.  Although shear 
blade quenching is easy to operate, but easy to collapse in the blade in the use , the service life of the cutting edge is shorter. 
After making use of T10A steel blade, since adopting shell quenching, improved the fatigue properties, and
 collapse edge tended to decrease,and the service life of shear blade extended to 7 times .
14.Used for guide pin, guide sleeve, pushing board, pushing plate guide bush, quenching hardness 50 to 55 HRC.
15.Used for plastic mould, slider, locking wedge pin, quenching hardness 54-58 HRC.
16.Used to push rod, tube, quenching hardness 54-58 HBC.
17.Used for charging room, plunger, quenching hardness 50 to 55 HRC.
18.Used for core, convex mold, mold plate, insert, quenching hardness between 46 ~ 52 HRC, also be used for thermosetting 
plastics mold of small core and etc.
19.Suitable for production with high abrasion resistance and smaller thermosetting plastic molding mold.