Udimet L-605（UNS R30605）
1.Composition(wt%)
|
C
|
Cr
|
Ni
|
Fe
|
W
|
Co
|
Mn
|
Si
|
S
|
P
|
|
0.05-0.15
|
19.0-21.0
|
9.0-11.0
|
≦3.0
|
14.0-16.0
|
balance
|
1.0-2.0
|
≦0.4
|
≦0.03
|
≦0.04
|
2.Physical Properties
|
Density
（g/cm3）
|
Melting point
（℃）
|
Specific heat capacity
（J/kg·℃）
|
Electric resistivity
（Ω·cm）
|
Thermal conductivity
（W/m·℃）
|
|
9.27
|
1300-1410
|
385
|
88.6×10E-6
|
9.4
|
3.Mechanical Properties
Instantaneous rupture properties（bar，typical hot treatment）
|
Test temperature
℃
|
Tensile strength
MPa
|
Yield strength
(0.2yield point)MPa
|
Elongation
%
|
|
20
|
994
|
466
|
50
|
High temperature endurance properties（bar，typical hot treatment）
|
Test temperature
℃
|
Test time
h
|
Burst pressure
MPa
|
|
649
|
1000
|
270
|
|
704
|
1000
|
220
|
|
760
|
1000
|
160
|
|
816
|
1000
|
120
|
|
871
|
1000
|
72
|
|
927
|
1000
|
44
|
|
982
|
1000
|
25
|
4.Applications
1.Used in industrial furnace parts.
2.Used in gas turbine components.
|